The La0.75Sr0.25Cr0.5Mn0.5O3-δ (LSCM) catalyst and the novel Ru/La0.75Sr0.25Cr0.5Mn0.5O3-δ composite were investigated as alternative anodes for the direct utilization of propane in anode-supported solid oxide fuel cells. In particular, their synthesis and performance in direct propane reforming were studied. The LSCM powders were prepared by a sol-gel method based on a modified Pechini procedure. Single-phase LSCM perovskite powders were obtained. SEM micrographs of the LSCM powders revealed particles in the 200-300 nm range with a homogeneous grain distribution. The deposition of 5 wt.% metallic ruthenium nanoparticles on the LSCM perovskite powders was carried out by a microwave-assisted procedure. TEM investigations of Ru/LSCM composites showed a homogeneous distribution of metallic ruthenium nanoparticles with a mean grain size of around 2-3 nm. The catalytic activity of these potential anode materials was investigated for the following propane reforming processes: steam reforming (SR), autothermal reforming (ATR) and partial oxidation (POX) at 600, 700 and 800 °C. Very high propane conversion rates were observed under POX and ATR conditions at 700 and 800 °C for both the LSCM and Ru/LSCM compounds (> 92 at 700 °C and > 98% at 800 °C), whereas in the steam reforming environment, a satisfactory conversion was achieved only at 800 °C. The ruthenium presence was found to strongly improve the selectivity for H2 and syngas production for all of the experiments performed, reaching an approximately 90% syngas yield. Finally, good chemical stability after the catalytic tests was demonstrated for the LSCM and Ru/LSCM anode materials.

Novel Ru/La0.75Sr0.25Cr0.5Mn0.5O3-δ catalysts for propane reforming in IT-SOFCs

ANTONUCCI, Pierluigi;
2010-01-01

Abstract

The La0.75Sr0.25Cr0.5Mn0.5O3-δ (LSCM) catalyst and the novel Ru/La0.75Sr0.25Cr0.5Mn0.5O3-δ composite were investigated as alternative anodes for the direct utilization of propane in anode-supported solid oxide fuel cells. In particular, their synthesis and performance in direct propane reforming were studied. The LSCM powders were prepared by a sol-gel method based on a modified Pechini procedure. Single-phase LSCM perovskite powders were obtained. SEM micrographs of the LSCM powders revealed particles in the 200-300 nm range with a homogeneous grain distribution. The deposition of 5 wt.% metallic ruthenium nanoparticles on the LSCM perovskite powders was carried out by a microwave-assisted procedure. TEM investigations of Ru/LSCM composites showed a homogeneous distribution of metallic ruthenium nanoparticles with a mean grain size of around 2-3 nm. The catalytic activity of these potential anode materials was investigated for the following propane reforming processes: steam reforming (SR), autothermal reforming (ATR) and partial oxidation (POX) at 600, 700 and 800 °C. Very high propane conversion rates were observed under POX and ATR conditions at 700 and 800 °C for both the LSCM and Ru/LSCM compounds (> 92 at 700 °C and > 98% at 800 °C), whereas in the steam reforming environment, a satisfactory conversion was achieved only at 800 °C. The ruthenium presence was found to strongly improve the selectivity for H2 and syngas production for all of the experiments performed, reaching an approximately 90% syngas yield. Finally, good chemical stability after the catalytic tests was demonstrated for the LSCM and Ru/LSCM anode materials.
2010
IT-SOFC; Propane reforming; Sol-gel
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.12318/3568
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 23
  • ???jsp.display-item.citation.isi??? ND
social impact