Fe2O3 and Fe2O3:Ge nanofibers (NFs) were prepared via electrospinning and thoroughly characterized via several techniques in order to investigate the effects produced by germanium incorporation in the nanostructure and crystalline phase of the oxide. The results indicate that reference Fe2O3 NFs consist of interconnected hematite grains, whereas in Fe2O3:Ge NFs, constituted by finer and elongated nanostructures developing mainly along their axis, an amorphous component coexists with the dominant α-Fe2O3 and γ-Fe2O3 phases. Ge4+ ions, mostly dispersed as dopant impurities, are accommodated in the tetrahedral sites of the maghemite lattice and probably in the defective hematite surface sites. When tested as anode active material for sodium ion batteries, Fe2O3:Ge NFs show good specific capacity (320 mAh g−1 at 50 mA g−1) and excellent rate capability (still delivering 140 mAh g−1 at 2 A g−1). This behavior derives from the synergistic combination of the nanostructured morphology, the electronic transport properties of the complex material, and the pseudo-capacitive nature of the charge storage mechanism.

Effect of germanium incorporation on the electrochemical performance of electrospun Fe2O3 nanofibers-based anodes in sodium-ion batteries

C. Triolo;S. Santangelo
2021-01-01

Abstract

Fe2O3 and Fe2O3:Ge nanofibers (NFs) were prepared via electrospinning and thoroughly characterized via several techniques in order to investigate the effects produced by germanium incorporation in the nanostructure and crystalline phase of the oxide. The results indicate that reference Fe2O3 NFs consist of interconnected hematite grains, whereas in Fe2O3:Ge NFs, constituted by finer and elongated nanostructures developing mainly along their axis, an amorphous component coexists with the dominant α-Fe2O3 and γ-Fe2O3 phases. Ge4+ ions, mostly dispersed as dopant impurities, are accommodated in the tetrahedral sites of the maghemite lattice and probably in the defective hematite surface sites. When tested as anode active material for sodium ion batteries, Fe2O3:Ge NFs show good specific capacity (320 mAh g−1 at 50 mA g−1) and excellent rate capability (still delivering 140 mAh g−1 at 2 A g−1). This behavior derives from the synergistic combination of the nanostructured morphology, the electronic transport properties of the complex material, and the pseudo-capacitive nature of the charge storage mechanism.
2021
ELECTROSPUN FIBRES, IRON (III) OXIDES, GERMANIUM INCORPORATION, SODIUM ION BATTERIES, RAMAN SPECTROSCOPY, NEUTRON DIFFRACTION, XAS, EXAFS
File in questo prodotto:
File Dimensione Formato  
Petrovičovà_2021_ApplSci_Effect_editor.pdf

accesso aperto

Descrizione: Articolo principale
Tipologia: Versione Editoriale (PDF)
Licenza: Creative commons
Dimensione 2.18 MB
Formato Adobe PDF
2.18 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.12318/85400
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 6
  • ???jsp.display-item.citation.isi??? 5
social impact